Changzhou DLX Alloy Co., Ltd.
1. We are able to design and develop products based on customer needs, and meet customer requirements by providing appropriate engineering drawings or samples. 2. We can provide the product within one
Add to Cart
0Cr21Al4 resistance wire is a type of iron chromium aluminum alloy resistance wire, which has good high-temperature stability and oxidation resistance, and is therefore widely used in many fields.
By being applied in the automotive industry, 0Cr21Al4 resistance wire enhances the performance, safety, and comfort of vehicles, providing essential support for their normal operation and driving experience.
0Cr21Al4 resistance wire is widely used as heating elements in automotive heaters to heat coolant and maintain stable temperatures for both the engine and the cabin.
0Cr21Al4 resistance wire serves as a crucial component in automotive seat heaters to provide seat heating functionality, enhancing passenger comfort.
0Cr21Al4 resistance wire is used in heaters and sensors within automotive HVAC systems to control temperature and humidity.
0Cr21Al4 resistance wire is used as resistor components within Automotive Engine Control Units (ECUs) for precise measurement and adjustment of sensors and control systems.
0Cr21Al4 resistance wire is used in resistive spark plugs within automotive ignition systems to provide reliable ignition performance and long-term durability.
| Alloy Nomenclature Performance | 1Cr13Al4 | 0Cr25Al5 | 0Cr21Al6 | 0Cr23Al5 | 0Cr21Al4 | 0Cr21Al6Nb | 0Cr27Al7Mo2 | |
| Main Chemical composition | Cr | 12.0-15.0 | 23.0-26.0 | 19.0-22.0 | 20.5-23.5 | 18.0-21.0 | 21.0-23.0 | 26.5-27.8 |
| Al | 4.0-6.0 | 4.5-6.5 | 5.0-7.0 | 4.2-5.3 | 3.0-4.2 | 5.0-7.0 | 6.0-7.0 | |
| Re | opportune | opportune | opportune | opportune | opportune | opportune | opportune | |
| Fe | Rest | Rest | Rest | Rest | Rest | Rest | Rest | |
| Nb0.5 | Mo1.8-2.2 | |||||||
| Max. continuous service temp. of element(°C) | 950 | 1250 | 1250 | 1250 | 1100 | 1350 | 1400 | |
| Resistivity at 20ºC(μΩ·m) | 1.25 | 1.42 | 1.42 | 1.35 | 1.23 | 1.45 | 1.53 | |
| Density(g/cm3) | 7.4 | 7.1 | 7.16 | 7.25 | 7.35 | 7.1 | 7.1 | |
| Thermal conductivity(KJ/m·h·ºC) | 52.7 | 46.1 | 63.2 | 60.2 | 46.9 | 46.1 | ||
| Coefficient of lines expansion(α×10-6/ºC) | 15.4 | 16 | 14.7 | 15 | 13.5 | 16 | 16 | |
| Melting point approx.( ºC) | 1450 | 1500 | 1500 | 1500 | 1500 | 1510 | 1520 | |
| Tensile strength(N/mm2) | 580-680 | 630-780 | 630-780 | 630-780 | 600-700 | 650-800 | 680-830 | |
| Elongation at rupture(%) | >16 | >12 | >12 | >12 | >12 | >12 | >10 | |
| Variation of area(%) | 65-75 | 60-75 | 65-75 | 65-75 | 65-75 | 65-75 | 65-75 | |
| Repeat Bending frequency(F/R) | >5 | >5 | >5 | >5 | >5 | >5 | >5 | |
| Hardness(H.B.) | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | |
| Continuous Servicetime(Hours/ ºC) | -- | ≥80/1300 | ≥80/1300 | ≥80/1300 | ≥80/1250 | ≥50/1350 | ≥50/1350 | |
| Micrographic structure | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | |
| Magnetic properties | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | |
| ||
| ||
| ||
| ||
| ||